Polyamide and nylon

Polyamide is one of the most popular 3D printing materials used by professional 3D printing companies. Its advantages are manifold: it is available at a reasonable price, it can include interlinking and interlocking parts, and it can be finished in various ways (dyed, smoothed, spray-painted, given a velvet finish). Today we will explain why Polyamide is such a great all-rounder and how 3D printing in nylon plastic really works.

The Base Material: It All Starts With Powder

Unlike with most home printers, Polyamide prints are not created using a plastic filament. In fact, Polyamide models are constructed from a white, very fine, granular powder. This powder-based material will give you unbelievable design freedom… and as you can see below it will give us quite some work freeing the sintered models from the un-sintered powder. But we will come back to that in just a minute.

Moving on, it is important to note that the powder used by 3D printers cannot be any kind of powder. Since it will be used for ultra-thin printing layers, the powder must be perfectly shaped in order to even out. Consider rocks and marbles; you could easily put rocks on top of each other to build a pyramid. However, building a pyramid with marbles would be way more difficult, as the perfectly shaped spheres would just even out and your pyramid wouldn’t stand a chance. Similar to the marbles, the polyamide powder needs to have the perfect shapes of spheres since each and every printing layer needs to have exactly the same height (and we’re talking about microns here).

Another important feature of the powder is its melting point, which is set at 170°C/338°F. You will see in a second why this detail matters.

The Printing Process: Laser Sintering

To create your 3D print, a laser in the printer melts the Polyamide powder together. So here’s how it works: A super-thin layer of polyamide is spread out by a roller. The print chamber of the 3D printer then heats up to a temperature slightly below 170°C/338°F. At this point, the powder does not melt since it has not reached its melting point. And now the magic happens: a laser touches those areas of the layer that are part of your design, raising the temperature of those areas just above 170°C/338°F, and voilà, your part is sintered (well, one layer of your part). The 3D printer will continue to spread out one layer of powder after another, and the laser will systematically touch the correct spots of each layer and sinter the object together.

To observe this process in action, take a look at the following video:

After the Printing: Cooldown and Digging

While the printing process itself can take up to 1.5 days, the cooldown phase can take even longer. Once the printing job is done, it is not possible to immediately grab the 3D prints – the cooldown can take up to two days. Once this period is over, the result is a big block of powder with the sintered models contained inside. This means that we need to start digging for the printed parts.

The Final Touch: Finishing Your 3D Print

Once the above steps have been completed, post-production processes will begin.

First, your 3D prints will be cleaned with vacuum cleaners and high-pressure air guns. Since your object was created within a comfy bed of powder, there are no support structures that need to be cut away.

Second, we will apply the finish of your choice (the exact steps depend heavily on the choice you made when placing your order). Your Polyamide print can be polished, dyed, spray-painted, or get a velvet finish. You can take a look at all of our 26 options for Polyamide here.